Aegis® H35ZI is an unfilled, low viscosity, non-lubricated nylon 6 injection molding homopolymer exhibiting excellent melt flow properties for filling thin sections and reduced cycle times. It exhibits good strength, stiffness and toughness as well as excellent heat, chemical and abrasion resistance.

Polymer Name: Polyamide 6 (PA 6)

Processing Methods: Injection Molding

Additives Included: Lubricant (Unspecified)

Flexural Modulus: 2465.0 - 2465.0 MPa

Technical Data Sheet

Ask AdvanSix Questions

Thomas Clark avatarEd Asirvatham avatarJohn Facinelli avatar

Enhanced TDS

Identification & Functionality

Additives Included
Chemical Family
Polymer Name
Plastics & Elastomers Functions
Technologies

Features & Benefits

Applications & Uses

Plastics & Elastomers Processing Methods
Processing Guidelines

Material Handling

Aegis® H35ZI homopolymer is supplied in sealed containers and drying prior to processing is not required. However, high moisture is the primary cause of processing problems. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80°C (176°F) is recommended. Drying time is dependent on moisture level.

Properties

Physical Form
Typical Properties
ValueUnitsTest Method / Conditions
96% SAV2.39
Rockwell Hardness119Scale RASTM D-785
Coefficient of Linear Thermal Expansion72μm/mm °CASTM D-831
Density1.12g/cm3ASTM D-792
Elongation Break (at 23°C (73°F))75%ASTM D-638
Elongation Yield (at 23°C (73°F))4.1%ASTM D-638
Extractable Contentmax. 0.8%SOP-702-307
Flexural Modulus (at 23°C (73°F))2,465 (357,518)MPa (psi)ASTM D-790
Flexural Strength (at 23°C (73°F))96 (13,924)MPa (psi)ASTM D-790
Heat Deflection (at 264 psi (1.8 MPa))47 (117)°C (°F)ASTM D-648
Heat Deflection (at 66 psi (0.45 MPa))152 (306)°C (°F)ASTM D-648
Melt Flow Rate (at 235°C/1.0 kg (455°F/1.0 kg))22.7g/10 minASTM D-1238
Melting Point222 (432)°C (°F)ASTM D-3418
Moisture (24 Hour)1.6%ASTM D-570
Moisture (50% RH)2.7%ASTM D-570
Moisture (Saturation)9.5%ASTM D-570
Moisture Contentmax. 0.10%ASTM D-6869
Mold Shrinkage Linear Flow1.27%ASTM D-955
Notched Izod Impact (at 23°C (73°F))46J/m (ft-lbs/in)ASTM D-256
Notched Izod Impact (at -40°C (-40°F))45J/m (ft-lbs/in)ASTM D-256
Tensile Modulus (at 23°C (73°F))2750 (398,854)MPa (psi)ASTM D-638
Viscosity (FAV)38 +/- 3ASTM D-789
Yield Tensile Strength (at 23°C (73°F))79 (11458)MPa (psi)ASTM D-638

Technical Details & Test Data

Injection Molding Guidelines

Typical Profile

Melt Temperature: 240-280°C (464-536°F)
Mold Temperature: 80-95°C (176-203°F)
Injection and Packing Pressure: 35-125 bar (500-1500 psi)

Mold Temperatures

A mold temperature of 80-95°C (176-203°F) is recommended, but temperatures as low as 10°C (50°F) can be used where applicable.

Pressures

Injection pressure controls the filling of the part and should not be applied for 90% of ram travel. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off.

Fill Rate

Fast fill rates are recommended to ensure uniform melt delivery to the cavity and to prevent premature freezing.